喷气包芯纱的纺制及其包覆效果探析-中国纱线网.doc

喷气包芯纱的纺制及其包覆效果探析 邢明杰 杨 磊 李永霞 孙福纪 (青岛大学) (山东省纺织职业技术学院) (东华大学) (山东省渚诚中纺金维纺织有限公司) 摘要： 以35．5 tex(33．66 dtex)棉涤包芯纱为例，介绍了喷气包芯纱的纺纱工艺流程、各工序工艺参数配置及采取的技术措施。探讨了纱与环锭包芯纱的成纱质气纺纱的包覆机理，分析了影响喷气包芯纱包覆效果的主要因素。对喷气包芯纱与环锭包芯纱的成纱质量进行了对比，结果表明，喷气包芯纱强力不匀率小，包覆效果较好。 关键词：喷气纺纱；包芯纱；工艺参数；成纱质量；包覆机理；分析 中图分类号：TS104．1 文献标识码：A 文章编号：1001—7415(2005)09-0001-04 Discussion on Spinning Air-jet Core-spun Yarn and Its Covered Effect Xing Ming]ie Yang Lei (Qingdao University) (Shandong Textile Vocational Technology lnstitute) Li Yongxia Sun Fuji (Donghua University) (Shamhong Zhucheng Chinatex G-way Textile Co.,Ltd.) Abstract Taking 35．5 tex(3 3．66dtex) cotton polyester corc-spun yarn as example．spinning technology circulation, technology parameters of each process and technique measures of air-iet core-spun yarn were introduced. Covered mechanism of air-jet spinning was discussed, and main factors which influence on covered effect of aur-jet spinning were also analyzed. Yarn forming quality of air-jet core-spun yarn was compared with that of ring core-spun yarn, and the result shows that air-iet core-spun yarn has lower stenght irregularity and better covered effect. Key Words Air-jet Spinning Yarn, Core-spun Yarn, Technology Parameter, Yarn Forming Quality, Covered Mechanism, Analysis 包芯纱是一种以长丝为纱芯(也可以短纤维纱为纱芯)外包短纤维的复合纱，包芯纱充分利用了各种纤维的优势与特点，喷气纺纱是通过高速回转的压缩气流对须条进行假捻包缠成纱的，持殊的成纱机理使喷气纱具有特殊的成纱结构，从而使得利用喷气纺纺制包芯纱具有一定优势。下面以35．5 tex(3 3．66 dtex)棉涤喷气包芯纱品种为例，就生产情况及成纱性能作一分析介绍。 l 喷气包芯纱的纺制 1．1 原料 喷气包芯纱所用的棉纤维应长而细、短纤维含量低，棉纤维的长度越长、细度越细，可纺喷气纱的号数也就越细，可纺性能越好。对喷气包芯纱适纺性能影响较大的是原棉中短纤维的含量，因此应尽可能去除短绒和杂质，尽可能使纤维平行伸直。本次试纺所使用的棉纤维为新疆产长绒棉，细度1．65dtex，主体长度30．7 mm，单纤维强力4．04 c N，断裂长度24．43 k m。 芯纱采用涤纶长丝，其细度由所纺纱号决定。一般纺纱号数大，涤纶长丝细度就大。为了保证成纱的包覆率，涤纶长丝细度应偏小掌握。本次试纺选用涤纶长丝细度为3 3．66 dtex，断裂强力ll 6．6 cN，断裂伸长率22．1％。 1．2 工艺流程 喷气纺纱机有粗纱喂入和条子喂入两种方式，试纺采用条子喂入。其前纺工艺流程采用环锭纺精梳工艺，工艺流程如下： 棉：A002型抓棉机→A006 B型棉箱混棉机→A034型六辊筒开棉机→A036 B型豪猪式开棉机→A092A型双棉箱给棉机→A076C型单打手成卷机→Al86D型梳棉机→A272A型并条机→Al9