碳纳米管石墨烯的制备.ppt

结构：单层石墨片绕一定的中心卷曲而成的中空、无缝纳米级管直径：1-6nm长度：几百nm~几?m，甚至mm特性：无层间交互作用超级力学性能（钢的100倍）极强的吸附性能优异的储氢特性高的比表面积Advantage:easilyscalabletolargedimensions;achievesanalmost100%single-atomiclayergraphenecoverageofadesiredsubstrate;havedistincttransportcharacteristicsShortcoming:limitedbythesizeofthesubstrateandthegrowthchamberCitygases:CH4,C2H6,C3H8,n-C4H10,et.al.SynthesisMWCNTsfromnatureresourcesEndoet.al.ChemSusChem2008,1,820SiO2,FeO,Fe2O3,Al2O3,andothersGarnetpowder:催化剂优势Highquality（lowID/IG）UniformelectronicpropertyalongonetubePossibilityofcreatingintegratedcircuitsonindividualcarbonnanotubes取向和超长SWCNTs关键：Introductionsuitablealigningforce电场取向气流取向晶格取向取向和超长SWCNTs手性矢量(n,m)：n-m=3k→m-tube(1/3)n-m≠3k→s-tube(2/3)s-tube：diameter?bandstructures-tube?FETsm-tube?Interconnections后处理直接生长(原位)Zhanget.al.Carbon49(2011),2555Kizeket.al.J.Mater.Chem.2011l,DOI:10.1039/c1jm12254aCNTs的直径与手性控制CNTs的直径与手性控制介电泳Krupke,etal.Science301,344(2003);后处理DNA辅助的离子交换色谱Zhenget.al.NatureMaterials2,338(2003)甲烷等离子体刻蚀Daiet.al.Science314,974(2006)CNTs的直径与手性控制后处理凝胶法分离Tanakaet.al.NanoLett.,2009,9,1497“透明胶带”法分离Zhanget.al.Angew.Chem.Int.Ed.2011,50,6819直接生长CNTs的直径与手性控制电场辅助生长Zhanget.al.Carbon49(2011),2555UV辅助生长Choiet.al.JACS2009,131,14642CNTs的直径与手性控制直接生长CNT“克隆”Zhanget.al.NanoLett.,2009,9,1673合成环对苯结构Itamiet.al.Angew.Chem.Int.Ed.2010,49,10202SiO2催化，控制直径和精确定位Huanget.al.2009,131,2094石墨烯的合成石墨烯的合成机械球磨辅助液相剥离法物理方法VerónicaLeón.etal.ACSNano,2014,8,563石墨烯的合成高定向热解石墨MingshengXu.etal.ACSNano,2011,5,1522SWCNT、MWCNT、G的三篇最早报道的文献SW/MW都是电弧放电，SW的电极需要铁催化剂；G机械剥离*CNT的发展（各种应用），圈了几个你可以提下，比如CNT的发现、做纤维、做CNT阵列、做反应催化剂、做能量电池，就是说一下名字*左上是FewerlayersgrapheneFETs（少层数石墨烯做的场效应晶体管）左下是石墨烯做的水凝胶，做法是将石墨氧化后，再水热还原（就是在特定反应器里180℃加热12h）得到，力学很好，电容也不错右面是氧化石墨烯（GO）悬浮液用铁还原成石墨烯纳米片层的悬浮液