连铸连轧.doc

内蒙古科技大学 连铸连轧工艺 结课作业 学 院：材料与冶金学院 专 业：材料成型及控制工程 班 级：成型2013-2班 姓 名：吴蕊 学 号：1361105225 薄板坯连铸连轧工艺技术发展的概况 摘　要：薄板坯连铸连轧工艺问世10年来发展迅速,CSP、ISP、FTSR为代表的各种工艺技术的发展各具特色。总的发展趋势是,提高铸机生产能力充分发挥后部连轧机的生产能力;改进品种质量,提高产品的市场覆盖率;采用无头轧制工艺、生产超薄规格产品,以取代部分冷轧产品的市场;应用范围扩大,越来越多的在以高炉铁水为原料的大型联合企业中得到应用,为该工艺的发展开拓了更广阔的前景。关键词：薄板坯　连铸连轧　发展趋势 Survey of Technological Development of Thin SlabContinuous Casting and Rolling Zhang Shaoxian(Wuhan Iron & Steel Design Research Institute) Abstract：Technology of thin slab continuous casting and rolling has been rapidly developped these ten years since its invention.some typical process technologics,such as CSP,ISP and FISR,etc.have been developped with their own characteristics.The overall development tendency is:1)to increase concaster capability to make full use of caster;2)to improve product quality to increase product marketability;3)to produce super thin products with endless rolling process technology to take place of some cold-rolled products in market; 4)to enlarge applications in order to make it widely used in large joint ventures with hot metal as raw material.As a result ,this process will have great expectations in future developmentKeywords：thin slab　continuous casting and rolling　development tendency▲ 1　前　言 　　自1989年美国纽科格拉福特斯维尔厂第一条CSP薄板坯连铸连轧生产线投产至今的10年中,又相继有CSP、FTSR、CONROOL、TSP等类型的生产线相继投入生产。薄板坯连铸连轧技术的成功应用和发展,是20世纪最后10年中在钢铁生产方面最具有重大意义的技术革新。　　　薄板连铸连轧工艺与常规的工艺相比,由于它具有节能、投资省、生产周期短、劳动成本低及适应性强等优点,故引起了全世界的重视。据统计全球各地已建成投产及在建的薄板坯连铸共约50流,总生产能力为5228万t/a。 2　几种主要类型的技术特点及其发展 2.1　CSP工艺技术 　　世界第一条CSP生产线薄板坯连铸连轧生产线已于1989年建成投产,因其工艺开发早,技术成熟,工艺及设备相对较简单可靠,故实际应用也最多。至1997年末,SMS已签定的合同已有27流铸机。　　CSP技术的主要特点是采用立弯式铸机漏斗形结晶器,最初的铸坯很薄,一般为40～50mm,未采用液芯压下,后部设辊底式隧道炉作为铸坯的加热均热及缓冲装置,采用5～6架精轧机,成品带钢最薄为1～2mm。　　近10年中CSP铸机的单量已从初期的80～90万t/a提高到如美国的纽科厂3号铸机能力150万t/a。为了提高生产能力和改进铸铸坯的质量,铸坯的厚度根据用户情况有所增加,并采用了液芯压下技术。美国Dynamics厂1995年12月投产的一流CSP铸机坯厚度70mm,第一次采用了液芯压下技术。我国正在建设的邯郸钢厂CSP铸坯厚度为60～80mm,因铸坯加厚而采用了1架粗轧和5架精轧的轧机组成。随着铸坯的厚度的增加及拉速的提高,铸坯的冶金长度也相应增加。现SMS对铸坯厚度大于70mm的铸机也设计了直结晶器